PA6 1030B 日本宇部PA6 挤出级PA6 拉丝料
| |
PA6 1030B 日本宇部兴产株式会社 物性数据 |
①原料描述部分
| 规格级别： |
--- |
外观颜色： |
--- |
| 用途概述： |
--- |
| 备注说明： |
特性：高粘度 |
②原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
--- |
ASTM D-570 |
1.8 |
% |
| 吸水率 |
--- |
ASTM D-570 |
10.7 |
% |
| 成型收缩率 |
--- |
UBEmethod |
1.2 |
% |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
1.14 |
--- |
| 薄膜厚度 |
--- |
--- |
50 |
µm |
| 薄雾 |
--- |
--- |
3 |
% |
| 光泽 |
--- |
--- |
140 |
% |
| 静态磨擦 |
--- |
--- |
1.0 |
--- |
| 机械性能 |
断裂下的伸张率 |
--- |
--- |
620 |
% |
| 模压力 |
--- |
--- |
4700 |
kgf/cm2 |
| 屈服下的伸张强度 |
--- |
--- |
200 |
kgf/cm2 |
| 断裂下的伸张强度 |
--- |
--- |
780 |
kgf/cm2 |
| TABER磨耗率 |
--- |
ASTM D-1044 |
7 |
mg |
| 屈服下的伸张强度 |
-30° |
ASTM D-638 |
1100 |
kgf/cm2 |
| 屈服下的伸张强度 |
-30° |
ASTM D-638 |
870 |
kgf/cm2 |
| 屈服下的伸张强度 |
23° |
ASTM D-638 |
750 |
kgf/cm2 |
| 屈服下的伸张强度 |
23° |
ASTM D-638 |
400 |
kgf/cm2 |
| 屈服下的伸张强度 |
80° |
ASTM D-638 |
320 |
kgf/cm2 |
| 屈服下的伸张强度 |
80° |
ASTM D-638 |
180 |
kgf/cm2 |
| 断裂下的伸张强度 |
23° |
ASTM D-638 |
>720 |
kgf/cm2 |
| 屈服下的延伸率 |
23° |
ASTM D-638 |
8 |
% |
| 断裂下的延伸率 |
23° |
ASTM D-638 |
>200 |
% |
| 弯曲强度 |
-30° |
ASTM D-790 |
1400 |
kgf/cm2 |
| 弯曲强度 |
-30° |
ASTM D-790 |
1300 |
kgf/cm2 |
| 弯曲强度 |
23° |
ASTM D-790 |
1100 |
kgf/cm2 |
| 弯曲强度 |
23° |
ASTM D-790 |
400 |
kgf/cm2 |
| 弯曲强度 |
80° |
ASTM D-790 |
400 |
kgf/cm2 |
| 弯曲强度 |
80° |
ASTM D-790 |
250 |
kgf/cm2 |
| 弯曲弹性率 |
-30° |
ASTM D-790 |
35000 |
kgf/cm2 |
| 弯曲弹性率 |
-30° |
ASTM D-790 |
33000 |
kgf/cm2 |
| 弯曲弹性率 |
23° |
ASTM D-790 |
25000 |
kgf/cm2 |
| 弯曲弹性率 |
23° |
ASTM D-790 |
7000 |
kgf/cm2 |
| 弯曲弹性率 |
80° |
ASTM D-790 |
7000 |
kgf/cm2 |
| 弯曲弹性率 |
80° |
ASTM D-790 |
4000 |
kgf/cm2 |
| 抗冲击强度 |
-30° |
ASTM D-256 |
5.0 |
kgf.cm/cm |
| 抗冲击强度 |
23° |
ASTM D-256 |
7.5 |
kgf.cm/cm |
| 抗冲击强度 |
23° |
ASTM D-256 |
50 |
kgf.cm/cm |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
120 |
--- |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
85 |
--- |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
85 |
--- |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
55 |
--- |
| 挤剪强度 |
23° |
ASTM D-732 |
650 |
kgf/cm2 |
| 挤剪强度 |
23° |
ASTM D-732 |
600 |
kgf/cm2 |
| 1%变形下的压缩强度 |
23° |
ASTM D-695 |
200 |
kgf/cm2 |
| 1%变形下的压缩强度 |
23° |
ASTM D-695 |
100 |
kgf/cm2 |
| 电气性能 |
体积电阻率 |
--- |
ASTM D-257 |
1015 |
Ω.cm |
| 体积电阻率 |
--- |
ASTM D-257 |
1012 |
Ω.cm |
| 绝缘耐力 |
--- |
ASTM D-149 |
20 |
KV/mm |
| 介电常数 |
60HZ |
ASTM D-150 |
3.9 |
--- |
| 介电常数 |
60HZ |
ASTM D-150 |
9.0 |
--- |
| 介电常数 |
103HZ |
ASTM D-150 |
3.8 |
--- |
| 介电常数 |
103HZ |
ASTM D-150 |
8.0 |
--- |
| 介电常数 |
106HZ |
ASTM D-150 |
3.5 |
--- |
| 介电常数 |
106HZ |
ASTM D-150 |
4.5 |
--- |
| 介电损耗 |
60HZ |
ASTM D-150 |
0.01 |
--- |
| 介电损耗 |
60HZ |
ASTM D-150 |
0.10 |
--- |
| 介电损耗 |
103HZ |
ASTM D-150 |
0.02 |
--- |
| 介电损耗 |
103HZ |
ASTM D-150 |
0.10 |
--- |
| 介电损耗 |
106HZ |
ASTM D-150 |
0.02 |
--- |
| 介电损耗 |
106HZ |
ASTM D-150 |
0.12 |
--- |
| 热 性 能 |
燃烧率 |
--- |
UL94 |
V-2 |
--- |
| 热变形温度 |
4.6kgf/cm2 |
ASTM D-648 |
170 |
°C |
| 熔点 |
DSC |
--- |
215-225 |
°C |
| 线性热膨胀系数 |
--- |
ASTM D-696 |
8 |
X的10-5cm/cm/°C |
| 热变形温度 |
18.6kgf/cm2 |
ASTM D-648 |
65 |
°C |
| 其它性能 |
氧气 |
--- |
--- |
25 |
me/m2.24h |
点击图片查看大图